Composition and use of 5052 alloy aluminum plate

The main alloy element of 5052 alloy aluminum plate is magnesium, which has excellent forming and processing function, corrosion resistance, weldability and medium strength. It is used to make aluminum sheet metal parts of aircraft fuel tank, oil pipe, traffic vehicle and ship, appearance, street lamp bracket, rivets, hardware products, electrical shell, etc.

5052 aluminium alloy sheet is widely used in marine applications :such as ships, automobiles, aircraft welding parts, Metro Light rails. Pressure containers (such as liquid tankers, refrigerated trucks, refrigerated containers), refrigeration devices, TV towers, drilling settings, transportation settings, missile components, armor and so on, which need to be strictly fireproof.

5052 aluminium sheet has excellent oral processing quality, and pre-polishing/mirror polishing is used in the way of aluminium coil, so there is no need to adopt extra finishing method. It is an ideal material for large-scale electronic products such as notebook computers and television.

What are the chemical compositions of 5052 aluminium sheet plate ?

Copper-copper: 0.10; magnesium: 2.2-2.8;

Aluminum Al: residual; Silicon Si: 0.25;

Zinc and zinc: 0.10; Manganese and manganese: 0.10;

Tensile Strength of 5052 aluminum plate (_b): 170~305 MPa

Compliance strength_0.2 (MPa) > 65

Modulus of Elasticity (E): 69.3-70.7 Gpa

The annealing temperature is 345 C.

Hardness index of 5052 aluminium plate: 3880.3-2006, mechanical scale only listed: tensile, compliance, epitaxy and bending R angle, no hardness delimitation, may refer to EN 485-2:2004, 052 Brinell hardness HBW: 47-83.

5052 aluminum plate: Aluminum and aluminum alloy extruded bars (<150mm, H112, T6, O)

Features of 5052 aluminum plate: Al-Mg alloy aluminum plate with high strength, fatigue strength, plasticity and corrosion resistance, but without heat treatment.

5052 aluminium sheet has low plasticity, poor cutting function and can be polished when it is cold and hard.